Hongye Silicone HY-916 Ultra Soft Pad Printing Silicone 14 Shore A
HY-916 is the lowest hardness model in Hongye Silicone pad printing series, 14±2A shore hardness, conforms to irregular curved surfaces for complete pattern transfer. Excellent elasticity with 570% elongation, pads recover quickly after compression. Condensation cure, 30 to 40 minutes operation time, 3 to 4 hours cure time.
Core Selling Points
• 14±2A shore hardness, lowest in the series • 570% elongation, excellent elasticity and quick recovery • 25±2kN/m tear strength, long pad service life • Uniform ink pickup, clear pattern transfer • For irregular curved surfaces and precision fine patterns • Gentle on scratch sensitive surfaces • Room temperature cure, easy operation
Technical Parameters
Model: HY-916 | Color: White | Hardness: 14±2 Shore A | Viscosity: 36000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 3.5 MPa | Tear Strength: 25±2 kN/m | Elongation: 570% | Mix Ratio: 100:2~100:3 | Density: 1.10±0.03 g/cm3 Model: HY-901 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 3.8 MPa | Tear Strength: 22±2 kN/m | Elongation: 380% | Mix Ratio: 100:2~100:3 | Density: 1.12±0.03 g/cm3 Model: HY-902 | Color: White | Hardness: 30±2 Shore A | Viscosity: 35000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 4.0 MPa | Tear Strength: 24±2 kN/m | Elongation: 430% | Mix Ratio: 100:2~100:3 | Density: 1.15±0.03 g/cm3 Model: HY-912 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Operation Time: 30-40 min | Cure Time: 3-4 h | Tensile Strength: 4.0 MPa | Tear Strength: 25±2 kN/m | Elongation: 340% | Mix Ratio: 100:2~100:3 | Density: 1.13±0.03 g/cm3
Application Scenarios
Electronic product housings, mobile phone cases, earphone cases with irregular curved surfaces and fine LOGO patterns, scratch sensitive sprayed or electroplated surfaces. Toys, gifts, anime figures, children toys with diverse shapes and soft rubber or PVC materials prone to indentations.
Operation Instructions
- Clean mold, apply release agent
- Weigh 100:2 to 100:3 ratio
- Stir 3 to 5 minutes, avoid bubbles
- Vacuum degas 2 to 3 minutes
- Pour into mold, stand at room temperature
- Cure 3 to 4 hours, demold, use after 24 hours
Selection Guide
HY-901 economy 30A for flat patterns, HY-902 balanced 30A for conventional use, HY-912 high tear 30A for large area high frequency, HY-916 ultra soft 14A for curved surfaces and precision patterns.
Recommended Application
Ultra soft pad printing for electronic housings, toys and gifts with irregular curved surfaces.
Quality and Compliance
ISO 9001 certified, COA reports, RoHS and REACH compliant.
Packaging
1kg, 5kg, 20kg, 25kg, 200kg iron drum.
Competitive Advantages
Own production line, monthly output 100 tons, factory direct sales, fast delivery.
Ordering and Logistics
T/T and PayPal, sample service, 1 to 3 working days delivery, express air sea freight.
Technical Support
Experienced team, custom formulation available.
Precautions
Wear gloves, avoid nitrogen sulfur tin contact, accurate weighing.
Storage
Cool dry place, 5 to 35 degrees, 12 months shelf life.
FAQ
Q: Will low hardness pads break easily? A: Tear strength 25kN/m and 570% elongation ensure long life. Q: Suitable for large area? A: Better for curved surfaces, choose HY-912 for large flat area. Q: Sticky surface after cure? A: Check curing agent ratio and mixing, ensure dry environment.