HY-912 Multi Color Pad Printing Silicone High Tear Strength
HY-912..，
HY-912 multi color pad printing silicone is a condensation cure two component RTV silicone with tear strength 25±2 kN/m, designed for multi color overprinting and fine pattern transfer on toys and electronic housings. Consistent ink pickup, clean release, long pad life.
Quantity
HY-912 is specially engineered for multi color overprinting and fine pattern printing. High tear strength 25±2 kN/m ensures durable pads. Tensile 4.0 MPa, elongation 340% for good resilience and surface conformity. Viscosity 32000±2000 mPa.s, working time 30-40 min, cure time 3-4 h. Widely used on plastic toys, electronic housings, craft gifts.
Core Features
• Tear strength 25±2 kN/m
• Tensile 4.0 MPa, elongation 340%
• Consistent ink pickup and clean release
• Linear shrinkage ≤0.3%
• Excellent ink and solvent resistance
Technical Parameters
Model: HY-912 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 4.0 MPa | Tear: 25±2 kN/m | Elongation: 340% | Mix Ratio: 100:2~100:3 | Density: 1.13±0.03 g/cm3
Model: HY-901 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 3.8 MPa | Tear: 22±2 kN/m | Elongation: 380% | Mix Ratio: 100:2~100:3 | Density: 1.12±0.03 g/cm3
Model: HY-902 | Color: White | Hardness: 30±2 Shore A | Viscosity: 35000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 4.0 MPa | Tear: 24±2 kN/m | Elongation: 430% | Mix Ratio: 100:2~100:3 | Density: 1.15±0.03 g/cm3
Model: HY-916 | Color: White | Hardness: 14±2 Shore A | Viscosity: 36000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 3.5 MPa | Tear: 25±2 kN/m | Elongation: 570% | Mix Ratio: 100:2~100:3 | Density: 1.10±0.03 g/cm3
Application Scenarios
Multi color overprinting on plastic toys and fine pattern printing on electronic housings. High tear strength resists aging during repeated ink contact.
Application and Operation Instructions
Prepare clean mold and materials
Weigh A and B at 100:2 to 100:3
Mix thoroughly 2-3 min
Degas in vacuum 3-5 min
Pour slowly into mold
Cure 3-4 h at room temp, rest 24 h
Selection Guide
HY-901: economy general use. HY-902: high wear high volume. HY-912: multi color fine patterns. HY-916: ultra soft complex curves.
Recommended Application
Multi color overprinting on plastic toys and electronic housings.
Quality and Compliance
ISO 9001 certified, COA with each batch, RoHS REACH compliant, exported to 80+ countries.
Packaging
A: 20/25/200kg drums. B: 1kg bottles. 1kg trial packs available. OEM supported.
Competitive Advantages
Own factory, monthly 100+ tons, 30%+ lower than imports, free technical support, OEM low MOQ.
Ordering and Logistics
T/T PayPal, free 1kg sample freight collect, 1-3 days stock shipment, non dangerous goods, COA and MSDS included.
Technical Support
Engineers 10+ years experience, custom formulation MOQ 50kg, full lifecycle support.
Precautions
Wear gloves, avoid tin sulfur amine, accurate weighing, thorough mixing, cure 15-35°C, ventilated area.
Storage
Cool dry 5-30°C, 12 months shelf life, reseal after use, B can be refrigerated.
FAQ
Q: Pad life? A: 100K-150K prints under normal use.
Q: Color bleeding? A: Clean pad between colors, HY-912 consistent transfer helps.
Q: Bubbles? A: Vacuum degas 3-5 min, pour slowly.
• Tear strength 25±2 kN/m
• Tensile 4.0 MPa, elongation 340%
• Consistent ink pickup and clean release
• Linear shrinkage ≤0.3%
• Excellent ink and solvent resistance
Technical Parameters
Model: HY-912 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 4.0 MPa | Tear: 25±2 kN/m | Elongation: 340% | Mix Ratio: 100:2~100:3 | Density: 1.13±0.03 g/cm3
Model: HY-901 | Color: White | Hardness: 30±2 Shore A | Viscosity: 32000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 3.8 MPa | Tear: 22±2 kN/m | Elongation: 380% | Mix Ratio: 100:2~100:3 | Density: 1.12±0.03 g/cm3
Model: HY-902 | Color: White | Hardness: 30±2 Shore A | Viscosity: 35000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 4.0 MPa | Tear: 24±2 kN/m | Elongation: 430% | Mix Ratio: 100:2~100:3 | Density: 1.15±0.03 g/cm3
Model: HY-916 | Color: White | Hardness: 14±2 Shore A | Viscosity: 36000±2000 mPa.s | Op Time: 30-40 min | Cure: 3-4 h | Tensile: 3.5 MPa | Tear: 25±2 kN/m | Elongation: 570% | Mix Ratio: 100:2~100:3 | Density: 1.10±0.03 g/cm3
Application Scenarios
Multi color overprinting on plastic toys and fine pattern printing on electronic housings. High tear strength resists aging during repeated ink contact.
Application and Operation Instructions
Prepare clean mold and materials
Weigh A and B at 100:2 to 100:3
Mix thoroughly 2-3 min
Degas in vacuum 3-5 min
Pour slowly into mold
Cure 3-4 h at room temp, rest 24 h
Selection Guide
HY-901: economy general use. HY-902: high wear high volume. HY-912: multi color fine patterns. HY-916: ultra soft complex curves.
Recommended Application
Multi color overprinting on plastic toys and electronic housings.
Quality and Compliance
ISO 9001 certified, COA with each batch, RoHS REACH compliant, exported to 80+ countries.
Packaging
A: 20/25/200kg drums. B: 1kg bottles. 1kg trial packs available. OEM supported.
Competitive Advantages
Own factory, monthly 100+ tons, 30%+ lower than imports, free technical support, OEM low MOQ.
Ordering and Logistics
T/T PayPal, free 1kg sample freight collect, 1-3 days stock shipment, non dangerous goods, COA and MSDS included.
Technical Support
Engineers 10+ years experience, custom formulation MOQ 50kg, full lifecycle support.
Precautions
Wear gloves, avoid tin sulfur amine, accurate weighing, thorough mixing, cure 15-35°C, ventilated area.
Storage
Cool dry 5-30°C, 12 months shelf life, reseal after use, B can be refrigerated.
FAQ
Q: Pad life? A: 100K-150K prints under normal use.
Q: Color bleeding? A: Clean pad between colors, HY-912 consistent transfer helps.
Q: Bubbles? A: Vacuum degas 3-5 min, pour slowly.